copy of ΕΝΕΡΓΟ ΚΑΘΑΡΙΣΤΙΚΟ ΤΖΑΜΙΩΝ
ZINC SPRAY
ZINC SPRAY LIGHT COLOUR 400ML
Long-term protection and repair of metal surfaces
Excellent corrosion protection
Metal is actively protected, even when minor damage occurs
More than 100 hours of salt spray resistance (DIN 50021 SS)
Excellent adhesion properties on uncovered metal
Excellent properties for spot welding
Announcement
Not suitable for use as an adhesive base for synthetic materials
PU, MS polymers and hybrid sealants.
local_shipping FREE shipping on orders over 90.00 € and up to 2.0 Kgr. Details
Area of application
For visual improvement, repair and protection of metal surfaces from corrosion.
Instructions
The optimum application temperature is between 15 °C and 25 °C
Contents
400 ml
Chemical base
Acrylic resin
Colour
Silver grey
Min. solidification time
24 h
Full cure/solidification conditions
20°C
Resistance to salt spray test
400 h
Max. temperature resistance
400 °C
Powder drying time
10 min
Thickness of dry layer (first movement back and forth)
20 in
Conditions for powder drying time
at 20°C
Zinc content of dry film
80 %
Coating thickness
20 µm
Recoatable/dyeable
Conventional, preliminary testing required
Holding force conditions
at 20°C
Substrates with good adhesion
Ferrous metals
Galvanised surfaces
Spot weldable
Yes
Cross cut test
MAN 0-1
Cross cutting conditions
according to ISO 2409
Conditions for resistance to salt spray test
according to DIN EN ISO 9227
Service life from production
36 months(month)